superalloy
推荐文章
n.
超耐热合金；超合金；
英英释义
Superalloy
Nickel superalloy jet engine ([[RB199) turbine blade]]
以上来源于:Wikipedia
权威例句
Nickel based superalloy welding practices for industrial gas turbine applicationsRhenium additions to a Ni-base superalloy: Effects on microstructure
Creep of CMSX-4 superalloy single crystals: effects of misorientation and temperature
Creep resistance of CMSX-3 nickel base superalloy single crystals
Assessment of material damage in a nickel-base superalloy using nonlinear Rayleigh surface waves
Improvement of Creep strength in a nickel-base single-crystal superalloy by heat treatment
Solution heat treatment response of a third generation single crystal Ni-base superalloy
Experimental characterization of fatigue damage in a nickel-base superalloy using nonlinear ultrasonic waves
High temperature resistant part, made of single-crystal or polycrystalline nickel-base superalloy
The effect of uniaxial stress on the periodic morphology of coherent gamma prime precipitates in nickel-base superalloy crystals
1. The nozzle, which is cast in K465 cast superalloy by investment casting, is one of the key components of the airspace engine.
涡轮导向器是在研某型号航天发动机的关键部件，采用K465铸造高温合金无余量整体熔模铸造而成。
www.dictall.com
2. Glazing oxide film that could decrease shear stress and change its distribution could alleviate fretting wear of K417 nickel base superalloy.
通过降低剪切应力的大小和改变其分布形式，釉质氧化膜可以缓解K417镍基合金的微动磨损。
dict.cnki.net
3. Possibility to dope Y2O3 particle on the surface of superalloy sample and the relationship between homogeneity and irradiation parameters of laser have been investigated by means of laser irradiation.
本文通过激光辐照的方法，研究了在高温合金试样表面掺杂Y_2O_3质点的可能性、均匀程度与激光辐照参数的关系。
dict.cnki.net
4. After electron beam welding, electron beam local heat treatment was applied in GH4133 superalloy as the turbine disk material in this paper.
针对涡轮盘材料GH4133合金，在电子束焊后采用新颖的电子束局部热处理工艺对接头进行热处理。
www.dictall.com
5. The results can meet the requirements about qualitative analysis and semi-quantitative analysis of tungsten in superalloy.
研究结果可用于高温合金中钨元素的定性和半定量分析及材料牌号鉴别。
www.chemyq.com
6. The formation of the microstructure and the evolution process from dendrite into equiaxed structure during atomized process for spray formed superalloy were analyzed.
对喷射成形高温合金的组织形成及其从雾化过程的树枝晶向等轴晶组织的演变过程进行了分析。
dict.cnki.net
7. The critical deformation and forgeability of the spray formed superalloy were studied by wedge specimen and column specimen.
采用楔形试样和圆柱形试样分别研究了合金的临界变形和变形塑性。
www.dictall.com
8. By means of stereomicroscopy and scanning electronic microscopy(SEM), the fracture mode and mechanism of the broken K18 superalloy cast blade in a supercharger turbo were investigated.
采用体视显微镜、扫描电镜等分析手段对K18合金增压器涡轮铸造叶片的断裂形貌与断裂机制等进行了分析。
www.dictall.com
9. Transformation mechanism of carbides and their effect on the stress rupture property were investigated in a Ni-base single crystal superalloy with microcontent of carbon.
碳的镍基单晶高温合金在热处理和持久过程中的碳化物演化机制以及各种碳化物对合金持久性能的影响。
www.dictall.com
10. The effect of aging treatment on the tensile strength, elongation, hardness and microstructure of a cobalt base superalloy used for pistons rings was investigated in this paper.
本文研究了不同热处理时效温度和时效时间对一种活塞环用钴基高温合金的抗拉强度、延伸率、硬度及组织的影响。
www.dictall.com
11. The products by ESR include 243 designations of steel and superalloy.
产品包括优质合金钢与超级合金243个牌号。
dict.cnki.net
12. In order to study the fracture mechanism of IC6 superalloy, the tensile process of alloy was observed by back scatter image in situ.
为了研究IC6合金的断裂机制，用背散射电子图像原值观察该合金的动态拉伸过程。
dict.cnki.net
13. The undercooled DZ125 superalloy was investigated by the method of glass and molten salt purification combined with cycled superheating, the mechanism of purification by compound salt was discussed.
采用自制净化剂和循环过热相结合的办法，研究了不同净化剂对DZ125高温合金的净化效果，探讨了复合熔盐的净化机理。
www.dictall.com
14. Shanghai Fengqu Superalloy Co. , Ltd. is a well-known manufactory that specializing in the production of special alloy materials.
上海丰渠特种合金有限公司是一个研究、开发、生产特种合金材料的高新技术企业。
danci.911cha.org
15. Various parts made of GH202 and GH586 superalloy were ignited and combusted only in high pressure oxygen-enriched atmosphere for short time.
对GH202、GH586合金部件在高温富氧工况下极短时间内就发生燃烧事故的原因进行了分析。
dict.cnki.net
16. The high-cycle fatigue performance of different microstructures of aluminide coating-superalloy system has been studied at 900℃.
研究了几种不同结构的铝化物涂层的涂层-合金系统在900℃时的高周疲劳性能。
dict.cnki.net
17. The transverse tensile properties and fracture behaviour of the twist low angle boundary of DD6 single crystal superalloy were investigated at 760℃, 850℃ and 980℃.
在760℃，850℃和980℃温度条件下，研究了DD6单晶高温合金扭转小角度晶界的横向拉伸性能和断裂特征。
www.dictall.com
18. By using physicochemical phase analysis, the phase in a new directionally solidified superalloy resisting combustion gas corrosion with long life had been determined qualitatively and quantitatively.
采用物理化学相分析方法，对一种新研制的抗燃气腐蚀长寿定向凝固合金的相作了定性和定量分析。
dict.cnki.net
19. The case, which is cast in K423A superalloy by investment casting, is one of the core components of the aeroengine.
机匣是在研某型号航空发动机上的核心部件，采用铸造高温合金K423A无余量整体精密铸造而成。
dict.cnki.net
20. The abnormal large-volume inclusion defect existing in certain P/M superalloy product was researched and its institution, forming reason was also analyzed.
本文研究了镍基粉末冶金高温合金个别制件中出现的异常大尺寸夹杂物缺陷，分析了它的成分、形成原因。
www.dictall.com
21. The cyclic creep tests of a Nickel-base superalloy has been conducted on a High Temperature Electrical Creep Machine equipped with an External Digital Controler (EDC).
本文利用装配有EDC数字控制器的高温电子蠕变试验机开展了一种镍基高温合金的循环蠕变实验。
www.dictall.com
22. GH543 cobalt-free nickel base superalloy is finally selected from the final 12 compositions extracted through theoretical analysis.
无钴镍基高温合金GH543即是从理论分析的最终的12种成分中选择出来的。
dict.cnki.net
23. The results show that the LCF of DZ4 superalloy at 760℃ and 800℃ can be contributed to stress fatigue owing to the main elastic damage in LCF processing.
结果表明，DZ4 合金760℃和800℃下的低周疲劳属应力疲劳，其损伤以弹性损伤为主，弹性损伤与疲劳寿命具有很好的相关性。
www.dictall.com
24. The oxidation kinetics of Co based superalloy DZ40M in air at 900~1100℃ has been determined, and the oxide compositions at different exposure temperatures for various times have been examined by XRD.
测定了DZ40M钴基合金在900 ～1100 ℃空气中的氧化动力学曲线，观察分析了各温度下经不同时间氧化后合金的表面氧化物形貌和组成。
dict.cnki.net
25. The low cycle fatigue properties of second generation single crystal superalloy DD6 with different withdrawing rates at 760 ℃ were studied.
研究了不同的抽拉速率对第二代单晶高温合金DD6的760℃低周疲劳寿命的影响。
www.dictall.com
26. In order to improve the property of nickel base superalloy K38 used at high temperature, tests of hot dip with Al-Si-RE and oxidation resistance had been performed.
为了提高镍基高温合金K38的高温性能，我们对K38合金进行了热浸镀铝-硅-稀土处理，并进行了抗高温氧化试验。
dict.cnki.net
27. The impact toughness of the superalloy increased with the increase of the grain size on the premise of less changing of intragranular precipitation, grain boundary precipitation, etc.
在晶内、晶界沉淀等因素变化较小的前提下，随晶粒几何尺寸增大，合金的冲击韧性升高；
dict.cnki.net
28. Investigation of fatigue crack initiation and propagation has been carried out on smooth plate specimens of a nickel base cast superalloy treated by HIP.
本文对铸造镍基高温合金光滑板试样（经过热等静压处理）疲劳裂纹的形成与扩展进行了研究。
dict.cnki.net
29. Heat treatment conditions of the superalloy 4 have been determined by the analysis of the differential thermal curve (DTA).
通过差热曲线分析和组织形貌观察，确定出合金4的热处理工艺；
dict.cnki.net
30. Heat treatment conditions of the superalloy 4 have been determined by the analysis of the differential thermal curve (DTA).
通过差热曲线分析和组织形貌观察，确定出合金4的热处理工艺；
dict.cnki.net
31. Hot-rolled heat-resisting superalloy plates
GB/T14995-1994高温合金热轧钢板
-- 来源 -- 英汉 - 翻译参考[网络]
32. cast superalloy
铸造高温合金
-- 来源 -- 英汉 - 翻译参考[网络]
33. Forged heat-resisting superalloy disks
GB/T14997-1994高温合金锻制圆饼
-- 来源 -- 英汉 - 翻译参考[网络]
34. Methods of longitudinal fracture test for heat-resisting superalloy bars
GB/T14999.3-1994高温合金棒材纵向断口试验法
-- 来源 -- 英汉 - 翻译参考[网络]
35. iron-base superalloy
铁基高温合金
-- 来源 -- 英汉 - 翻译参考[网络]
36. Cold brawn heat-resisting superalloy bars
GB/T14994-1994高温合金冷拉棒材
-- 来源 -- 英汉 - 翻译参考[网络]
37. wrought superalloy
变形高温合金
-- 来源 -- 英汉 - 翻译参考[网络]
38. Heat-resisting superalloy blanks for forged rings
GB/T14998-1994高温合金环件毛坯
-- 来源 -- 英汉 - 翻译参考[网络]
39. Cold-Rolled heat-Resisting superalloy sheets
GB/T14996-1994高温合金冷轧薄板
-- 来源 -- 英汉 - 翻译参考[网络]
40. After electron beam welding, electron beam local heat treatment was applied in GH4133 superalloy as the turbine disk material in this paper.
针对涡轮盘材料GH4133合金,在电子束焊后采用新颖的电子束局部热处理工艺对接头进行热处理。
-- 来源 -- dict.cnki.net
superalloy